Assessment of reinforcing steels in concrete exposed to salination water by using NDT (half-cell potential)

Abstract

ABSTRACT

The behavior of steel bars in the concrete structure under salinated environments are differs from one environment to another, however as long the basis of electrolysis circuit is completed which consists of anode, cathode and electrolyte medium is presence in particular environment, the corrosion process can occur to any metal that were to be place along with this environment. In this study, investigation of severity in corrosion for a reinforcing steel in concrete for 4 type of water sources which is sea water, salt marsh water, river water and tap water were explored. Results of all 4 water mediums explain that the exposition of concrete to natural environment results in different pattern of corrosion behavior.  This relates to the conclusion of having similar grade of concrete not necessarily results in similar form of corrosion map. The easier water to penetrate through the concrete cube and create electrolysis circuit the more severe the concrete cube was affected with corrosion elements.

Abstrak

Tingkah laku batang keluli dalam bahan konkrit binaan di persekitaran kemasinan adalah berbeza dari satu persekitaran kepada yang lain, akan tetapi selagi mana litar elektrolisis dilengkapkan yang mana terdapat anod, katod dan bahantara elektrolit dalam persekitaran tertentu, proses kakisan boleh berlaku kepada sebarang logam yang diletakkan bersama persekitaran ini. Dalam kajian ini, siasatan kelampauan kakisan untuk batang keluli pengukuh dalam konkrit untuk 4 sumber jenis air yang merupakan air laut, air kawasan paya, air sungai dan air paip telah dibuat. Keputusan dari kesemua 4 medium air menjelaskan bahawa pameran konkrit kepada keputusan-keputusan alam sekitar di jiwa lain tingkah laku kakisan. Ini berkaitan dengan kesimpulan mempunyai gred serupa membubuh simen bukan semestinya menyebabkan di bentuk selari peta kakisan. Air lebih mudah akan meresapi kiub konkrit dan mewujudkan litar elektrolisis yang lebih teruk kiub konkrit telah terjejas dengan unsur-unsur kakisan.